Amandla aphezulu eSisamente esiphantsi seCorundum fireclay Refractory Insulation Castable
Isicelo: Ukufakwa kwesithando sokunyibilikisa i-aluminium
Itekhnoloji ye-furnace ye-metallurgical casting edibeneyo yindlela yokwakha i-furnace ye-metallurgical apho kusetyenziswa khona izinto ezingafunekiyo ukuphosa izinto ezingafunekiyo zomzimba we-furnace ngaxeshanye. Iimpawu zale teknoloji zikwimeko entle yesakhiwo sayo, akukho zihlanganisi zezitena, kunye namandla aphezulu ngokubanzi, ngoko ke umzimba we-furnace unobomi obude benkonzo. Zama le teknoloji kwezinye imizimba ye-furnace kwishishini le-metallurgical lasekhaya elingeyo-ferrous. Ubushushu bokusebenza be-furnace ejikelezayo bufikelela kwi-1200℃, kwaye ubushushu bokusebenza be-furnace ejikelezayo bufikelela kwi-1000℃. I-furnace ejikelezayo isebenzisa ukutyhilwa kunye nokondla phezulu kwe-furnace, i-furnace encinci isuswa ngesandla nge-slag ngeengcango ezintathu ze-furnace, kwaye i-furnace enkulu isetyenziswa ukususa i-slag ngoomatshini ngeengcango ezimbini ze-furnace. Izinto eziluhlaza zii-ingots ze-aluminium, ii-scrap cast bars, iiprofayili ze-scrap kunye nee-coil ze-aluminium ezijikeleziweyo. I-furnace nganye emileyo ikwanazo neengcango ezimbini ze-furnace ze-slagging kunye nemisebenzi yokucoca. Ngaphambili, umzimba we-furnace wawenziwe ngezitena ezingafunekiyo, kwaye ezinye iindawo zonakala lula, ngaloo ndlela zichaphazela ubomi kunye nokusebenza kakuhle kwemveliso yomzimba we-furnace. Ekwakhiweni kwewebhusayithi yeZhengzhou, isithando sokunyibilikisa i-aluminiyam sigalelwa kancinci ngezinto ezirhabaxa ezingenakuchatshazelwa ukuphucula ubomi benkonzo yomzimba wesithando.
(1) Isinyithi esingamanzisiyo
| Imodeli | I-BZL-90 | I-BZL-85 | I-BZL-80 | |
| Uhlalutyo lweeKhemikhali(%) | AL203 | ≥90 | ≥85 | ≥80 |
| Ubushushu obuphezulu bokusebenza (C) |
| 1700 | 1700 | 1600 |
| Uxinano (Kg/m3) | 110℃X24h | ≥3.0 | ≥2.9 | ≥2.85 |
| Amandla okuguquguquka (i-Mpa) | 110℃X24h | ≥12 | ≥10 | ≥10 |
| 1100℃X3h | ≥15 | ≥14 | ≥12 | |
| Amandla oxinzelelo (i-Mpa) | 110℃X24h | ≥75 | ≥70 | ≥65 |
| 1100℃X3h | ≥90 | ≥85 | ≥80 | |
| Utshintsho olusisigxina lomgca %) | 1100℃X3h | ± 0.35 | ± 0.35 | ± 0.35 |
| Iarhente yokumelana ne-aluminium %) |
| 3~5 | 3~5 | 3~5 |
| Sebenzisa iindawo | Umzantsi wesithando somlilo, udonga lwesithando somlilo olusezantsi, irampu yokukrala i-slag, i-chute, iladle ye-aluminium kunye nebhokisi yokukhupha igesi, njl. | |||
(2) Iifayibha zentsimbi eziphoswayo
| Imodeli | I-FHA-80 | I-FHA-75 | I-FHA-70 | |
| Uhlalutyo lweeKhemikhali(%) | AL203 | ≥80 | ≥75 | ≥70 |
| Ubushushu obuphezulu bokusebenza (C) |
| 1550 | 1500 | 1500 |
| Uxinano (Kg/m3) | 110℃X24h | ≥2.8 | ≥2.7 | ≥2.65 |
| Amandla okuguquguquka (i-Mpa) | 110℃X24h | ≥12 | ≥10 | ≥9 |
| 1100℃X3h | ≥14 | ≥12 | ≥10 | |
| Amandla oxinzelelo (i-Mpa) | 110℃X24h | ≥75 | ≥70 | ≥70 |
| 1100°X3h | ≥85 | ≥75 | ≥70 | |
| Utshintsho olusisigxina lomgca %) | 1100℃X3h | 士0.4 | 士0.4 | 士0.4 |
| Sebenzisa iindawo | Umnyango wesithando somlilokwayeumnyangokwayeezinye iindawo | |||
(3) Isamente ephantsi enokuphoswa
| Imodeli | LC-70 | LC-65 | LC-60 | |
| Uhlalutyo lweeKhemikhali(%) | AL203 | ≥70 | ≥65 | ≥60 |
| Ubushushu obuphezulu bokusebenza (C) |
| 1500 | 1400 | 1350 |
| Uxinano (Kg/m3) | 110℃X24h | ≥2.65 | ≥2.6 | ≥2.6 |
| Amandla okuguquguquka (i-Mpa) | 110℃X24h | ≥8 | ≥7 | ≥7 |
| 1100℃X3h | ≥10 | ≥9 | ≥7 | |
| Amandla oxinzelelo (i-Mpa) | 110℃X24h | ≥65 | ≥65 | ≥60 |
| 1100℃X3h | ≥75 | ≥75 | ≥70 | |
| Utshintsho olusisigxina lomgca %) | 1100℃X3h | 士0.45 | 士0.45 | 士0.45 |
| Sebenzisa iindawo | Isetyenziselwa isithando somlilophezulu-uphahla lodonga kunye nesithando somlilo kunye nezinye iindawo | |||
(4) Ikhaphukhaphu ekhanyayo
| Imodeli | I-QZ-0.7 | I-QZ-1.0 | I-QZ-1.5 | |
| Uxinano (Kg/m3) | 110℃X24h | ≥0.7 | ≥1.0 | ≥1.5 |
| Amandla oxinzelelo (i-Mpa) | 110℃X24h | ≥2 | ≥5 | 》16 |
| Ukuqhuba kobushushu | (700℃.W/mk) | 0.2 | 0.31 | 0.58 |
| Sebenzisa iindawo | Kwezinye iindawo zokwambathisa ezifana nodonga lwesithando kunye nophahla lwesithando | |||